PVB (Polyvinyl Butyral)

With its excellent adhesive and film-forming properties, its strong binding power and its outstanding optical transparency, polyvinyl butyrals are unquestionably a versatile thermoplastic material. 

JK-1000

  • With excellent adhesive film-forming properties and strong binding power.
  • More remarkable rust resisting than Zinc Phosphate coating and Inorganic Zinc.
  • No abnormality after 72 hours of salt spray test.
  • No abnormality after tested under -50’C extreme condition.
Anti-corrosive
  • With excellent adhesive film-forming properties and strong binding power.
Compatibility
  • All kinds of coating can be applied to the main coating.
Durability
  • Excellent abrasion resistance, elasticity, prevention of crack.
Product Usage
  • Set to touch drying 5-10 minutes.

The world first and the nation's first concept technology PVB resin applied!

With remarkable adhesion and anti-corrosive coating, it will help to maintain painting for a long time.

After  on rust steel plate, it passes the 72-hour salt spray test

Result of the test to detect 26 harmful substances. No harmful substance is detected.

When coated on rust steel plate, it changes surface rust and forms a hard anti-corrosive coating film.

Product features and advantages!

Other Company's Products

  • High-cost surface preparation.
  • Require sand blasting to SA-2.5.
  • Rigid power tool cleaning to ST-3.
  • Longer time to prepare.
  • Time-consuming.
  • Costly application.
  • Longer time to complete.

Our Company's Products

  • Low- cost surface preparation.
  • Minimum cleaning required, sand papering or wire brushing.
  • Removal of oil & other Contaminants.
  • Easy to prepare.
  • 2 coats system.
  • Low application cost.
  • Shorter time to complete.

Application Fields!

  • Painting preparation, repair of shipbuilding, crane anti-corrosive coating
  • Marin/Ship structures, weld, anti-corrosive.
  • Construction equipment, H beams, steel
    structures, steel bridges.
  • Steel reinforced, rust conversion and
    anti-corrosive coating
  • Expensive equipment maintenance
  •  Plant equipment welding seam anti-corrosive
  • Other power generation facilities external paining repair and anti-corrosive
  • Vehicles(Car) parts
  • Vehicles(Car)body structure
  • Chemical equipment
  • Trains
  • Piping, Chemical plant structure

JK-Urethane TC

A two component topcoat highly durable finish based on acrylic and polyurethane resin.

  • Excellent gloss retention.
  • Durability.
  • Chemical resistance.
  • Good applicability.

JK-IOZ Primer

This paint is an Inorganic Zinc Rich Primer coating based on ethyl silicate liquid and high content of Zinc dust. It provides excellent protection against corrosion in longer weathering exposure of steel structures. It is used as an internal coating for petroleum product storage tank.

  • Excellent abrasion resistance.
  • Chemical and oil resistance.
  • Heat resistance up to 400 ‘C.
  • Fast Drying.

JK-Phenolic

A high build type two component epoxy phenolic coating suitable for interior tank lining, resistance to petroleum products, crude oil, alkalis and weak acids.

  • Excellent adhesion properties.
  • Abrasion resistance.
  • Chemical resistance.
  • Toughness.

JK-Epoxy Primer

Modified epoxy paint, suitable for the application of corroded areas where optimum surface cleaning is hard to attain. A surface tolerant primer paint with strong coating adhesion is applicable to apply in a wide range of existing coating. 

  • Good impact and abrasion resistance.
  • Resistance to water, oil and chemical.
  • High solid, Self-priming.
  • Good applicability.

Abrasion Test by Wire Brushing

Results :
No delamination or damages on the paint film.

Heat Resistance by Torch Testing

Results :
No visual damages on paint film.

Adhesion Test by Pull-off Testing

Results :
Break up point 17.09 Mpa =
( 2,478.05 Psi )

Wire Brushing Abrasion Test Comparison

Results:
High build Epoxy paint worn out!